Top welding tricks: how to become a more skilled welder and how to pick the top welding equipment. If a ball forms on the end of your rod when welding you are doing something wrong. It is usually one or more of these things: Too long an arc… • Too much torch angle • Not enough amperage for the rod size • Bad filler rod angle • Or some combination of all of these things. The 2 things I see most often with noobs are too long an arc AND too much torch angle. A long arc sets TIG welding back a few decades because it’s more like gas welding with an oxyfuel torch. The heat is not concentrated and you get this big heated arc plume like you get with a gas welding torch. Why would you want that? Your arc length should not be much more than the diameter of your tungsten electrode. I know that’s pretty close and if you get too close you will be grinding electrodes more than you are welding. But if you want really good welds, you need to use a tight arc.
For TIG welding, the metal needs to be clean; no rust, scale, paint, etc: TIG welding is not nearly as forgiving as Mig or stick when it comes to dirty metal. For TIG welding, the metal needs to be clean; no rust, scale, paint, etc. that means hot rolled steel needs to be ground to shiny bright metal…not just polished over. Welding hot rolled steel without grinding will make you look bad. Don’t do it if there is a chance someone might see it. Windy conditions or drafts in the welding area and you will lose shielding coverage and get pinholes/porosity in the weld . If you have to TIG weld in windy conditions, you are going to have to spend some time making wind breaks out of cardboard, plastic, or whatever you can get. TIG welding will just not tolerate much of a breeze much less a gust of wind. And please don’t try to TIG weld with a coat hanger or gas welding rod. They will bubble and hiss.
Do a practice run. This may sound silly, but you’ll find that many professional welders do this before every pass. Get in the most comfortable position you can, with support blocks in place if helpful, and run your hands along the path they will traverse as you make the weld. You will often find that a slight adjustment of your position will allow you to make a longer pass, or to move your hands with less stress. Any strain in your position will have a negative impact on the weld. Also, you build valuable muscle memory when making your practice run, which will help keep everything on track when you make the ‘real’ pass. Clean a contaminated electrode immediately! Every welder will contaminate their electrode at some point, but it’s essential that you replace a contaminated electrode immediately. I usually keep a group of pre-sharpened electrodes right on my welding bench, so I can swap them out without having to walk to my grinder.
Searching for the best Welding Supplies? We recommend Welding Supplies Direct & Associate company TWS Direct Ltd is an online distributor of a wide range of welding supplies, welding equipment and welding machines. We supply Plasma Cutters, MIG, TIG, ARC Welding Machines and support consumables to the UK, Ireland and Europe.
Before you start welding, make sure all of your connections are tight — from the front of the MIG gun to the power pin attaching it to the power source. Also be certain there is no spatter buildup on your consumables and that you have a ground cable as close to the workspace as possible. Whenever possible, hook the ground cable on the weldment. If that is not possible, hook it to a bench. But remember: The closer it is to the arc, the better. If you have a questionable ground, it can cause the gun to overheat, impacting contact tip life and weld quality. In addition, regularly clean any shavings from the welding wire or debris that collects on your consumable parts and in your liner using clean compressed air.